The difference between normalizing and tempering:

1: (quenching + high-temperature tempering) = quenching and tempering: a heat treatment process used to improve the comprehensive mechanical properties of steel materials. Quenched and tempered parts mostly work under relatively large dynamic loads. They bear the effects of stretching, compression, bending, torsion or shearing. Some surfaces also have friction, requiring certain wear resistance and so on. Especially for large parts in heavy machinery manufacturing, quenching and tempering treatment is used more, and quenching and tempering treatment occupies a very important position in heat treatment.
Quenching and tempering is generally used on medium carbon steel, such as No. 45 steel.
2: Normalizing (obtaining sorbite structure, substantial pearlite): a heat treatment to improve the toughness of steel.
Normalizing is generally used on low carbon induction steel, such as No. 10 steel
3: Annealing: Slowly heat the metal to a certain temperature, keep it for a sufficient time, and then cool it at an appropriate speed. The purpose is to reduce hardness and improve machinability.
Commonly used quenched and tempered steels can be divided into four categories according to hardenability and strength:
1: Quenched and tempered steel with low hardenability
2: Quenched and tempered steel with medium hardenability
3: Quenched and tempered steel with high hardenability
4: Quenched and tempered steel with high hardenability

Parameters

technical standard:

Outer diameter accuracy: f7, f8, h7
Surface finish: ≦Ra0.4S
Roundness: ≦0.01mm
Straightness: ≦0.15/1000mm
Hard chrome plating thickness: 0.015~0.05mm (can be customized according to customer requirements)
Surface hardness: HB220-260
Standard outer diameter: ￠3~￠120
Standard length: 1000-6000mm
Material: S45C (45#), 40Cr, GCr15, 2Cr13, 42CrMo, SUS304, SUS303, SUS316, etc.

Luoyang Super Foliage Trading Company is a factory-based company where the original factory founded in 1993. In order to provide better services to customers, the new trading branch was formed in 2017. We are specializing in the products of cast iron, ductile iron, steel casting and nonferrous parts. It includes 10kg to over 10 tons investment casting and large casting partsctile .

Because of the factory background, we understand what the customer needs

we have better understanding and communication between customers and suppliers. Up to now, there are about over 10 best factories that work closely with us.